NO.	Item		Unit	Requirement
				3025	3027	323	PFCC3
1	Density		g/cm3	1.30 to 1.42	1.30 to 1.42	1.30 to 1.50	--
2	Martin¡¯s temperature			125	135	125	--
3	Tensile strength		MPa	65	60	98(Lengthwise)	--
4	Flexural strength		MPa	105	90	156.9(Lengthwise)	110
5	Bondig strength		N	5500	5500	--	--
6	Impact strength		kg/m2	25	20	34(Lengthwise)	7.0
7	Compressive Strength	Parallel to layer direction	MPa	--	--	245	--
		Perpendicular to layer direction		--	--	147	--
8	Breakdown strength perpendicular to layer direction, at 902oil		MV/m	2-4	5-8	--	--
9	Breakdown voltage parallel to layer direction, at 902		kV	--	10	--	--
10	Insulation Resistance	At room Temperature		--	1.0x104	--	--
	Parallel to layer direction	After being humidified		--	1.0x101	--	--
11	Water Absorption		%	--	--	1.0	186 to 540mg

Properties Requirements are shown in Table2

Nominal Thickness mm	Tolerance
	3025	3027	323	PEFCC3
0.4	--	--	--	0.12
0.5	0.15	0.15	0.10	0.13
0.6	--	--	0.10	0.14
0.8	0.15	0.15	0.10	0.15
1.0	0.15	0.15	0.10	0.16
1.2	0.18	0.18	0.15	0.17
1.5	0.18	0.18	0.15	--
1.6	--	--	--	0.19
1.8	0.23	0.23	0.20	--
2.0	0.23	0.23	0.20	0.21
2.5	0.33	0.30	0.30	0.24
3.0	0.33	0.30	0.30	0.26
3.5	0.33	0.30	0.30	--
4.0	0.38	0.35	0.40	0.32
4.5	0.38	0.35	--	--
5.0	0.48	0.40	0.50	0.36
5.5	0.48	0.40	--	--
6.0	0.58	0.50	0.60	0.80
6.5	0.58	0.50	--	--
7.0	0.68	0.55	0.60	--
8.0	0.68	0.55	0.60	0.98
9.0	0.80	0.65	0.60	--
10.0	0.80	0.65	0.70	1.12
12	1.00	0.80	0.70	1.28
14	1.00	0.80	0.80	1.40
16	1.30	1.10	0.80	1.52
20	1.30	1.10	1.00	1.74
25	1.50	1.20	1.50	2.04
30	1.50	1.20	1.50	2.24
35	2.00	1.50	2.00	2.48
40	2.00	1.50	2.00	2.70
45	2.80	2.00	2.50	2.90
50	2.80	2.00	2.50	3.10
60	--	2.50	3.00	3.50
70	--	2.80	3.00	3.80
80	--	2.80	--	4.20
90	--	--	--	4.50
100	--	--	--	4.80